Luminous nano-glass-ceramics used as white led source and preparing method of luminous nano-glass-ceramics

ABSTRACT

A luminous nano-glass-ceramics used as white LED source and the preparing method of nano-glass-ceramics are provided. The glass is a kind of non-porous compact SiO 2  glass in which luminous nano-microcrystalites are dispersed. The luminous nano-microcrystalite has the chemical formula of Y x Gd 3-x Al 5 O 12 :Ce, wherein 0≦x≦3. The stability of the said glass is good and its irradiance is uniform. The preparing method comprises the following steps: dissolving the compound raw materials in the solvent to form mixed solution, dipping the nano-microporous SiO 2  glass in the solution, taking it out and air drying, sintering at the temperature of 1100-1300° C. for 1-5 hours by stage heating, and obtaining the product. The method has a simple process, convenient operation and low cost.

FIELD OF THE INVENTION

The present invention belongs to the illumination and photo-electronic field, and relates to a luminescent glass and a method for the preparation thereof, and specifically relates to a luminescent nano-crystalline glass for white LED source, and a method for the preparation thereof.

BACKGROUND OF THE INVENTION

As light emitting diode (LED) has advantages such as long life, low energy consumption, and quick start, LED devices have been widely used in fields such as signal lights, automobile lights, large screen display and illumination. At present, the most commonly used white LED achieves white light by combining blue LED chips with fluorescent powders. The mechanism thereof is: blue light chips stimulate the fluorescent powders to emit yellow light, and blue light and yellow light complement with each other to produce a visible white light. The fluorescent powders currently used for white LED are mainly cerium-doped yttrium aluminum garnet (YAG:Ce) fluorescent powder, silicate fluorescent powder, nitride fluorescent powder, and the like, among which the YAG:Ce fluorescent powder is the most widely used. However, it is difficult to control the shape and particle size of the fluorescent powder, which leads to a high cost for manufacturing high-quality fluorescent powder for white LED. In addition, during the encapsulating process, fluorescent powder should be mixed with glue. In the mixture of fluorescent powder with glue, due to the poor compatibility of the two components, fluorescent powder tends to precipitate, resulting in non-uniform distribution of the glue, which in turn results in poor uniformity of the light emission of the LED device, and poor color tone consistency. This leads to a high cost of light separation for white LED. Due to the high cost and inconsistent property, the white LED materials used in many encapsulating factories in China still rely on importation.

SUMMARY OF THE INVENTION

The technical problem to be solved by the present invention is to overcome the defects in the prior art by providing a luminescent nano-crystalline glass for white LED source which has good stability, low cost, and uniform light emission.

The technical problem to be further solved by the present invention is to provide a method for manufacturing a luminescent nano-crystalline glass for white LED source, which is simple and facile, and the product thereof has stable qualities.

The technical solution of the present invention to solve the technical problem is: a luminescent nano-crystalline glass for white LED source, which is a non-porous compacted SiO₂ glass in which Y_(x)Gd_(3-x)Al₅O₁₂:Ce luminescent nano-crystalites are disperse, wherein 0≦x≦3.

In the luminescent nano-crystalline glass for white LED source, the luminescent nano-crystalline glass comprises a SiO₂ nano-porous glass as a substrate, and luminescent nano-crystalites having a formula of Y_(x)Gd_(3-x)Al₅O₁₂:Ce are dispersed in the pores of the SiO₂ nano-porous glass. After the SiO₂ nano-porous glass comprising the luminescent nano-crystalites is sintered, the pores shrink to form a non-porous compacted SiO₂ glass encapsulating Y_(x)Gd_(3-x)Al₅O₁₂:Ce luminescent nano-crystalites.

In the luminescent nano-crystalline glass for white LED source, the volume of the pores in the SiO₂ nano-porous glass represents 25˜40% of the total volume of the SiO₂ nano-porous glass.

In the luminescent nano-crystalline glass for white LED source, the SiO₂ nano-porous glass is substantially composed of the following components in weight parts:

SiO₂ 94.0~98.0 B₂O₃ 1.0~3.0 Al₂O₃ 1.0~3.0

The method for manufacturing the luminescent nano-crystalline glass for white LED source comprises the following steps:

(1) using at least one of oxides, nitrates, chlorides, sulfates, acetates of Y³⁺ and Gd³⁺; at least one of oxides, nitrates, chlorides, sulfates, acetates of Al³⁺; and at least one of oxides, nitrates, chlorides, sulfates, acetates of Ce³⁺ as raw materials, dissolving the raw materials in a solvent to prepare a mixed solution of ions of luminescent compounds, wherein the concentration of Al³⁺ is 0.5˜2 mol/L, the sum of the concentrations of Y³⁺ and Gd³⁺ is 0.3˜1.2 mol/L, and the concentration of Ce³⁺ is 0.001˜0.2 mol/L;

(2) selecting a SiO₂ nano-porous glass having interconnected pores as a substrate, wherein the volume of the pores in the SiO₂ nano-porous glass represents 25˜40% of the total volume of the SiO₂ nano-porous glass; and placing the SiO₂ nano-porous glass into the mixed solution obtained in step (1) and soaking for above 10 minutes;

(3) gradually heating the soaked SiO₂ nano-porous glass to 1100˜1300° C. and sintering for 1˜5 hours, to give the luminescent nano-crystalline glass for white LED source.

In the method for manufacturing the luminescent nano-crystalline glass for white LED source, when the raw materials are oxides of various ions, the solvent may be nitric acid, hydrochloric acid, sulfuric acid or acetic acid; when the raw materials are nitrates, chlorides, sulfates or acetates of various ions, the solvent may be water.

In the method for manufacturing the luminescent nano-crystalline glass for white LED source, in step (2), the SiO₂ nano-porous glass is placed into the mixed solution obtained in step (1) and soaked for 30 min˜5 h.

In the method for manufacturing the luminescent nano-crystalline glass for white LED source, in step (3), the soaked SiO₂ nano-porous glass is first air-dried under room temperature until the surface thereof becomes dry, and then placed in an oven and gradually heated up to 1150˜1250° C., and sintered at the same temperature for 2˜4 hours, cooled down with the oven to room temperature, and taken out to obtain the luminescent nano-crystalline glass for white LED source. In the temperature ranges of below 400° C. and above 900° C., the heating rate shall be no higher than 15° C./min.

In the method for manufacturing the luminescent nano-crystalline glass for white LED source, the SiO₂ nano-porous glass is substantially composed of the following components in weight parts: SiO₂ 94.0˜98.0, B₂O₃ 1.0˜3.0, and Al₂O₃ 1.0˜3.0.

The luminescent nano-crystalline glass of the present invention has Y_(x)Gd_(3-x)Al₅O₁₂:Ce luminescent nano-crystalites dispersed therein, and can emit yellow light under the stimulation of blue light, and can be used as a white LED source. In addition, Y_(x)Gd_(3-x)Al₅O₁₂:Ce luminescent nano-crystalites can be well dispersed in glass, which effectively lowers the non-radiation transition of luminescent ions in the glass and avoids concentration quenching effect caused by clusters. Furthermore, the volume of the pores represents 25˜40% of the total volume of the SiO₂ nano-porous glass, ensuring a sufficient amount of luminescent particles in the pores, and leading to good luminescent properties of the glass of the present invention. Furthermore, this kind of nano-porous glass substrate has good transparency for ultra-violet lights, which favors the absorption of stimulating lights by the luminescent particles, and thereby improves the luminescent efficiency.

SiO₂ nano-porous glass is used in the present invention as a substrate. Porous SiO₂ nano-porous glass material is suitable for preparing nano-materials. In particular, SiO₂ nano-porous glass is transparent in the visible light range, and therefore may be used as a substrate material for optically functional nano-particles. Due to the special pore structure of the SiO₂ nano-porous glass, luminescent particles in nano-scale may be prepared through the pores. During the sintering of the SiO₂ nano-porous glass, the pores shrink to encapsulate the luminescent particles, forming a compacted, non-porous, transparent nano-crystalline glass with high mechanical strength. In addition, as the luminescent particles are encapsulated in the glass, the product can be kept stable for a long time.

The luminescent nano-crystalline glass of the present invention has a high content of SiO₂, similar to that in quartz. Also similar to quartz, the luminescent nano-crystalline glass of the present invention has excellent physical and chemical properties, such as good chemical stability, high mechanical strength, low thermal expansion coefficient, resistance to thermal shock, and the like. These excellent properties render that the glass of the present invention may be used in many special fields, especially in severe environments, such as illumination and display in high-temperature, high-pressure, high-vibration and humid environments; high-power, high repetation frequency solid state laser field; long-term ourdoor solar energy material field; and the like.

In the process of manufacturing the luminescent glass by conventional high temperature melting, the compounds in the glass formation have high chemical activities, which would readily lead to the reaction between the compounds in the glass formation and the nano-particles, resulting in difficulties in preparing mono-dispersed luminescent nano-particles. In the present invention, the luminescent ions are introduced by soaking the SiO₂ nano-porous glass into a solution of the active ions, and a high-temperature solid-state sintering is carried out at 1100˜1300° C., which overcome the difficulties for preparing mono-dispersed luminescent nano-particles in quartz. The present invention gives a luminescent nano-crystalline glass with homogenous mono-dispersion, and provides a new route for preparing nano-materials, in particular a new method for preparing a luminescent nano-crystalline transparent glass material.

The Y_(x)Gd_(3-x)Al₅O₁₂:Ce luminescent nano-crystalline glass of the present invention has advantages such as simple preparation process, reliable product properties, and low cost. White LED encapsulation with this new luminescent material may solve many problems relating to the currently used mixed encapsulation of fluorescent powders and glue, and therefore has a great value for investment and a broad market of application.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is flow chart for manufacturing Y_(x)Gd_(3-x)Al₅O₁₂:Ce luminescent nano-crystalline glass;

FIG. 2 is the emission spectrum of the Y₃Al₅O₁₂:Ce nano-crystalline glass obtained in Example 1 under the stimulation of 460 nm blue light.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS EXAMPLE 1

Y₃Al₅O₁₂:Ce nano-crystalline glass is a non-porous compacted SiO₂ glass having luminescent nano-crystalites of formula Y₃Al₅O₁₂:Ce dispersed therein.

The Y₃Al₅O₁₂:Ce nano-crystalline glass is prepared according to the flow chart shown in FIG. 1. The preparation process is as follows. 1.149 g analytically pure Y(NO₃)₃.6H₂O (yttrium nitrate hexahydrate), 1.875 g analytically pure Al(NO₃)₃.6H₂O (aluminium nitrate hexahydrate) and 0.0043 g analytically pure Ce(NO₃)₃.6H₂O (cerium nitrate hexahydrate) are weighed with an analytical balance and dissolved in 10 ml of distilled water to prepare a mixed solution containing 0.3 mol/L Y³⁺, 0.5 mol/L Al³⁺ and 0.001 mol/L Ce³⁺. The SiO₂ nano-porous glass is placed into the mixed solution and soaked for 1 h, taken out and air-dried under room temperature until the surface thereof becomes dry, and placed into an oven. The oven is heated to 400° C. at 10° C./min, to 900° C. at 15° C./min and to 1200° C. at 5° C./min, and maintained at 1200° C. to sinter for 2 h. The sintered glass is cooled down with the oven to room temperature before being taken out. After cutting and polishing, the Y₃Al₅O₁₂:Ce nano-crystalline glass is obtained. FIG. 2 is the emission spectrum of the Y₃Al₅O₁₂:Ce nano-crystalline glass under the stimulation of 460 nm blue light, which indicates that this glass emits yellow light under the stimulation of blue light.

EXAMPLE 2

Y₃Al₅O₁₂:Ce nano-crystalline glass is a non-porous compacted SiO₂ glass having luminescent nano-crystalites of formula Y₃Al₅O₁₂:Ce dispersed therein.

The preparation process is as follows. 4.596 g analytically pure Y(NO₃)₃.6H₂O (yttrium nitrate hexahydrate), 7.500 g analytically pure Al(NO₃)₃.6H₂O (aluminium nitrate hexahydrate) and 0.868 g analytically pure Ce(NO₃)₃.6H₂O (cerium nitrate hexahydrate) are weighed with an analytical balance and dissolved in 10 ml of distilled water to prepare a mixed solution containing 1.2 mol/L Y³⁺, 2 mol/L Al³⁺ and 0.2 mol/L Ce³⁺. The SiO₂ nano-porous glass is placed into the mixed solution and soaked for 1 h, taken out and air-dried under room temperature until the surface thereof becomes dry, and placed into an oven. The oven is heated to 400° C. at 10° C./min, to 900° C. at 15° C./min, to 1200° C. at 5° C./min, and maintained at 1200° C. to sinter for 2 h. The sintered glass is cooled down with the oven to room temperature before being taken out. After cutting and polishing, the Y₃Al₅O₁₂:Ce nano-crystalline glass is obtained, which emits yellow light under the stimulation of blue light.

EXAMPLE 3

Y₃Al₅O₁₂:Ce nano-crystalline glass is a non-porous compacted SiO₂ glass having luminescent nano-crystalites of formula Y₃Al₅O₁₂:Ce dispersed therein.

The preparation process is as follows. 2.746 g analytically pure Y₂(SO₄)₃.8H₂O (yttrium sulfate octahydrate), 4.998 g analytically pure Al₂(SO₄)₃.18H₂O (aluminium sulfate octadecahydrate) and 0.202 g analytically pure Ce(SO₄)₂.4H₂O (cerium sulfate tetrahydrate) are weighed with an analytical balance and dissolved in 10 ml of distilled water to prepare a mixed solution containing 0.9 mol/L Y³⁺, 1.5 mol/L Al³⁺ and 0.05 mol/L Ce³⁺. The SiO₂ nano-porous glass is placed into the mixed solution and soaked for 8 h, taken out and air-dried under room temperature until the surface thereof becomes dry, and placed into an oven. The oven is heated to 400° C. at 10° C./min, to 900° C. at 15° C./min, to 1100° C. at 5° C./min, and maintained at 1100° C. to sinter for 4 h. The sintered glass is cooled down with the oven to room temperature before being taken out. After cutting and polishing, the Y₃Al₅O₁₂:Ce nano-crystalline glass is obtained, which emits yellow light under the stimulation of blue light.

EXAMPLE 4

Y₃Al₅O₁₂:Ce nano-crystalline glass is a non-porous compacted SiO₂ glass having luminescent nano-crystalites of formula Y₃Al₅O₁₂:Ce dispersed therein.

The preparation process is as follows. 0.135 g analytically pure yttrium xoide (Y₂O₃), 0.102 g analytically pure Al₂O₃ (aluminium oxide) and 0.172 g analytically pure CeO₂ (cerium oxide) are weighed with an analytical balance and dissolved in 10 ml of nitric acid to prepare a mixed solution containing 0.12 mol/L Y³⁺, 0.2 mol/L Al³⁺ and 0.1 mol/L Ce³⁺. The SiO₂ nano-porous glass is placed into the mixed solution and soaked for 10 h, taken out and air-dried under room temperature until the surface thereof becomes dry, and placed into an oven. The oven is heated to 400° C. at 10° C./min, to 900° C. at 15° C./min, to 1150° C. at 5° C./min, and maintained at 1150° C. to sinter for 2.5 h. The sintered glass is cooled down with the oven to room temperature before being taken out. After cutting and polishing, the Y₃Al₅O₁₂:Ce nano-crystalline glass is obtained, which emits yellow light under the stimulation of blue light.

EXAMPLE 5

Y_(1.5)Gd_(1.5)Al₅O₁₂:Ce nano-crystalline glass is a non-porous compacted SiO₂ glass having luminescent nano-crystalites of formula Y_(1.5)Gd_(1.5)Al₅O₁₂:Ce dispersed therein.

The preparation process is as follows. 0.910 g analytically pure YCI₃.6H₂O (yttrium chloride hexahydrate), 1.115 g analytically pure GdCl₃.6H₂O (gadolinium chloride hexahydrate), 2.414 g analytically pure AlCl₃.6H₂O(aluminium chloride hexahydrate) and 0.075 g analytically pure CeCl₃.7H₂O (cerium chloride heptahydrate) are weighed with an analytical balance and dissolved in 10 ml of distilled water to prepare a mixed solution containing 0.3 mol/L Y³⁺, 0.3 mol/L Gd³⁺, 1 mol/L Al³⁺ and 0.02 mol/L Ce³⁺. The SiO₂ nano-porous glass is placed into the mixed solution and soaked for 10 h, taken out and air-dried under room temperature until the surface thereof becomes dry, and placed into an oven. The oven is heated to 400° C. at 10° C./min, to 900° C. at 15° C./min, to 1200° C. at 5° C./min, and maintained at 1200° C. to sinter for 2 h. The sintered glass is cooled down with the oven to room temperature before being taken out. After cutting and polishing, the Y_(1.5)Gd_(1.5)Al₅O₁₂:Ce nano-crystalline glass is obtained, which emits yellow light under the stimulation of blue light.

EXAMPLE 6

YGd₂Al₅O₁₂:Ce nano-crystalline glass is a non-porous compacted SiO₂ glass having luminescent nano-crystalites of formula YGd₂Al₅O₁₂:Ce dispersed therein.

The preparation process is as follows. 0.676 g analytically pure Y(CH₃COO)₃.4H₂O (yttrium acetate tetrahydrate), 1.804 g analytically pure Gd(NO₃)₃.6H₂O (gadolinium nitrate hexahydrate), 3.75 g analytically pure Al(NO₃)₃.6H₂O (aluminium nitrate hexahydrate) and 0.087 g analytically pure Ce(NO₃)₃.6H₂O (cerium nitrate hexahydrate) are weighed with an analytical balance and dissolved in 10 ml of distilled water to prepare a mixed solution containing 0.2 mol/L Y³⁺, 0.4 mol/L Gd³⁺, 1 mol/L Al³⁺ and 0.02 mol/L Ce³⁺. The SiO₂ nano-porous glass is placed into the mixed solution and soaked for 24 h, taken out and air-dried under room temperature until the surface thereof becomes dry, and placed into an oven. The oven is heated to 400° C. at 10° C./min, to 900° C. at 15° C./min, to 1300° C. at 5° C./min, and maintained at 1300° C. to sinter for 5 h. The sintered glass is cooled down with the oven to room temperature before being taken out. After cutting and polishing, the YGd₂Al₅O₁₂:Ce nano-crystalline glass is obtained, which emits yellow light under the stimulation of blue light.

EXAMPLE 7

Gd₃Al₅O₁₂:Ce nano-crystalline glass is a non-porous compacted SiO₂ glass having luminescent nano-crystalites of formula Gd₃Al₅O₁₂:Ce dispersed therein.

The preparation process is as follows. 2.706 g analytically pure Gd(NO₃)₃.6H₂O (gadolinium nitrate hexahydrate), 3.75 g analytically pure Al(NO₃)₃.6H₂O (aluminium nitrate hexahydrate) and 0.434 g analytically pure Ce(NO₃)₃.6H₂O (cerium nitrate hexahydrate) are weighed with an analytical balance and dissolved in 10 ml of distilled water to prepare a mixed solution containing 0.6 mol/L Gd³⁺, 1 mol/L Al³⁺ and 0.1 mol/L Ce³⁺. The SiO₂ nano-porous glass is placed into the mixed solution and soaked for 10 h, taken out and air-dried under room temperature until the surface thereof becomes dry, and placed into an oven. The oven is heated to 400° C. at 10° C./min, to 900° C. at 15° C./min, to 1300° C. at 5° C./min, and maintained at 1300° C. to sinter for 2 h. The sintered glass is cooled down with the oven to room temperature before being taken out. After cutting and polishing, the Gd₃Al₅O₁₂:Ce nano-crystalline glass is obtained, which emits yellow light under the stimulation of blue light.

EXAMPLE 8

Y₃Al₅O₁₂:Ce nano-crystalline glass is a non-porous compacted SiO₂ glass having luminescent nano-crystalites of formula Y₃Al₅O₁₂:Ce dispersed therein.

The preparation process is as follows. 1.014 g analytically pure Y(CH₃COO)₃.4H₂O (yttrium acetate tetrahydrate), 1.020 g analytically pure Al(CH₃COO)₃ (aluminium acetate) and 0.0407 g analytically pure Ce(CH₃COO)₃.5H₂O (cerium acetate pentahydrate) are weighed with an analytical balance and dissolved in 10 ml of distilled water to prepare a mixed solution containing 0.3 mol/L Y³⁺, 0.5 mol/L Al³⁺ and 0.01 mol/L Ce³⁺. The SiO₂ nano-porous glass is placed into the mixed solution and soaked for 24 h, taken out and air-dried under room temperature until the surface thereof becomes dry, and placed into an oven. The oven is heated to 400° C. at 10° C./min, to 900° C. at 15° C./min, to 1200° C. at 5° C./min, and maintained at 1200° C. to sinter for 4 h. The sintered glass is cooled down with the oven to room temperature before being taken out. After cutting and polishing, the Y₃Al₅O₁₂:Ce nano-crystalline glass is obtained, which emits yellow light under the stimulation of blue light. 

1. A luminescent nano-crystalline glass for white LED source comprising a non-porous compacted SiO₂ glass in which luminescent nano-crystalites of formula Y_(x)Gd_(3-x)Al₅O₁₂:Ce are dispersed, wherein 0≦x≦3.
 2. The luminescent nano-crystalline glass for white LED source according to claim 1, wherein the luminescent nano-crystalline glass comprises the SiO₂ nano-porous glass, and luminescent nano-crystalites having the formula of Y_(x)Gd_(3-x)Al₅O₁₂:Ce are dispersed in the pores of the SiO₂ nano-porous glass; after the SiO₂ nano-porous glass comprising the luminescent nano-crystalites is sintered, the pores shrink to form the non-porous compacted SiO₂ glass encapsulating Y_(x)Gd_(3-x)Al₅O₁₂:Ce luminescent nano-crystalites.
 3. The luminescent nano-crystalline glass for white LED source according to claim 2, wherein the volume of the pores in the SiO₂ nano-porous glass represents 25˜40% of the total volume of the SiO₂ nano-porous glass.
 4. The luminescent nano-crystalline glass for white LED source according to claim 2, wherein the SiO₂ nano-porous glass is substantially composed of the following components in weight parts: SiO₂ 94.0~98.0 B₂O₃ 1.0~3.0 Al₂O₃  1.0~3.0.


5. A method for manufacturing a luminescent nano-crystalline glass for white LED source, comprising the following steps: (1) using at least one of oxides, nitrates, chlorides, sulfates, acetates of Y³⁺ and Gd³⁺; at least one of oxides, nitrates, chlorides, sulfates, acetates of Al³⁺; and at least one of oxides, nitrates, chlorides, sulfates, acetates of Ce³⁺ as raw materials, dissolving the raw materials in a solvent to prepare a mixed solution of ions of luminescent compounds, wherein the concentration of Al³⁺ is 0.5˜2 mol/L, the sum of the concentrations of Y³⁺ and Gd³⁺ is 0.3˜1.2 mol/L, and the concentration of Ce³⁺ is 0.001˜0.2 mol/L; (2) selecting a SiO₂ nano-porous glass having interconnected pores as a substrate, wherein the volume of the pores in the SiO₂ nano-porous glass represents 25˜40% of the total volume of the SiO₂ nano-porous glass; and placing the SiO₂ nano-porous glass into the mixed solution obtained in step (1) and soaking for above 10 minutes; (3) gradually heating the soaked SiO₂ nano-porous glass to 1100˜1300° C. and sintering for 1˜5 hours, to give the luminescent nano-crystalline glass for white LED source.
 6. The method for manufacturing the luminescent nano-crystalline glass for white LED source according to claim 5, wherein, when the raw materials are oxides of the ions, the solvent is selected from nitric acid, hydrochloric acid, sulfuric acid and acetic acid; and when the raw materials are nitrates, chlorides, sulfates or acetates of the ions, the solvent is water.
 7. The method for manufacturing the luminescent nano-crystalline glass for white LED source according to claim 5, wherein, in step (2), the SiO₂ nano-porous glass is placed into the mixed solution obtained in step (1) and soaked for 30 min˜5 h.
 8. The method for manufacturing the luminescent nano-crystalline glass for white LED source according to claim 5, wherein, in step (3), the soaked SiO₂ nano-porous glass is first air-dried under room temperature until the surface thereof becomes dry, and then placed in an oven and gradually heated up to 1150˜1250° C., and sintered at the same temperature for 2˜4 hours, cooled down with the oven to room temperature, and taken out to obtain the luminescent nano-crystalline glass for white LED source, wherein, in the temperature ranges of below 400° C. and above 900° C., the heating rate shall be no higher than 15° C./min.
 9. The method for manufacturing the luminescent nano-crystalline glass for white LED source according to claim 5, wherein the SiO₂ nano-porous glass is substantially composed of the following components in weight parts: SiO₂ 94.0˜98.0, B₂O₃ 1.0˜3.0, and Al₂O₃ 1.0˜3.0.
 10. The luminescent nano-crystalline glass for white LED source according to claim 3, wherein the SiO₂ nano-porous glass is substantially composed of the following components in weight parts: SiO₂ 94.0~98.0 B₂O₃ 1.0~3.0 Al₂O₃  1.0~3.0. 